Zertifizierung

CE, SGS, BV, TUV, ISO.

Anwendung

Clean PE/PP/OPP/BOPP Film bag, PP woven/nonwoven bag, composite film, with/without paint/ink.

Bedarf an Rohstoffen

Thickness: up to 500um. Bulk Density: 0.08~0.3 g/cm³. Moisture Residual: ≦7% by weight.

Endprodukt

PE PP pellet, granule size: Ф3*3mm, Moisture content 1-2%. Stacking density: 0.5-0.8 g/cm³.

Kapazität

Max. 180~250Kg/h (based on raw material condition and water content)

Parameter

Modell	PTCS80	PTCS100	PTCS130	PTCS150	PTCS185
Schraubendurchmesser (mm)	80	100	130	150	185
L/D	18-42
Drehzahl (U/min)	10-150
Ausgabe (KG/h)	150-250	200-350	450-600	600-700	800-1200
Stromverbrauch (kW/h)	90	130	220	270	366
Handbuch	1-2	1-2	2-3	2-3	2-4

Bauart der Maschine

Fütterungseinheit 1

Belt conveyor unit: The recycled waste can be directly placed on the conveyor belt to facilitate feeding, and the conveyor belt controls the feeding rate with ampere quantification.

Fütterungseinheit 2

Clamping wheelset: It can be matched with a belt conveyor unit to feed the entire roll of film on the rack simultaneously.

Schneideverdichtungsanlage

It is equipped with precise temperature control and a cutting system to ensure that the semi-molten plastic can quickly and stably enter the extrusion system for mixing and fusion.

Entgasungsloch

The double-degassing hole design of the extruder can release more ink and water vapor in the recycled material to improve the quality of the final product

System zur Änderung des Filtergitters

The double-column screen changing system has a filter area twice as large as the general pallet screen changing system. This screen-changing system can improve filtration efficiency and reduce the number of screen changes. In addition to reducing the number of screen changes, the dual-channel design allows the machine to continue to operate during the screen change process, increasing the overall production capacity of the machine and reducing waste.

Pelletieranlage

The hot die pelletizing system can immediately pelletize the melted plastic material after extrusion. Immediately after cutting the pellets, it enters the water ring for cooling. The particle shape and size are average, conducive to re-production in various extruders and injection molding machines.

The recycled particles of the product can be 100% directly put into the film-blowing machine or pipe extruder production line for reuse.